Youngjin Kim, Jaeryeong Lee
The leaching kinetics of zinc from zinc oxide-based metal oxide varistors (MOVs) was investigated in H2SO4 at atmospheric pressure. Kinetics experiments were carried out at various agitation speeds, particle sizes, initial H2SO4 concentrations, and reaction temperatures. It was determined that the leaching rate of zinc was independent of agitation speed above 300 rpm and also independent of particle size below 105 µm, whereas it dramatically increased with an increasing H2SO4 concentration. Except for when the H2SO4 concentration was varied, them-values were almost constant at varying agitation speeds (m-values: 0.554–0.579), particle sizes (m-values: 0.507–0.560) and reaction temperature (m-values: 0.530–0.560) conditions. All of them-values in these experiments were found to be below 0.580. Therefore, it is proposed that the extraction of zinc is a diffusion-controlled reaction. The leaching kinetics followed the D3 kinetic equation with a rate-controlling diffusion step through the ash layers, and the corresponding apparent activation energy was calculated as 20.7 kJ/mol in the temperature range of 313 K to 353 K.
@article{0c5f8a9d-2f6d-4e92-ada9-8610458f07ec,
title={Leaching Kinetics of Zinc from Metal Oxide Varistors (MOVs) with Sulfuric Acid},
author={Youngjin Kim and Jaeryeong Lee},
year={2016},
language={en}
}TY - JOUR TI - Leaching Kinetics of Zinc from Metal Oxide Varistors (MOVs) with Sulfuric Acid AU - Youngjin Kim AU - Jaeryeong Lee PY - 2016 LA - en ER -
Martina Laubertová, Bora Derin, Jarmila Trpčevská, Klaudia Šándorová and Emília Sminčáková
This study was performed to investigate the possibility of copper recovery from the waste printed circuit boards (WPCBs) of waste mobile phones using
İbrahim Sönmez, Kemal Şahbudak
Chalcopyrite (CuFeS2) is commonly used ore in the production of copper, but leaching of this ore is very slow and inefficient due to “passivation” dur
C.N. Mpinga, J.J. Eksteen
Platinum Group Metals (PGMs), often with associated gold, have very few occurrences where they are present in an ore deposit at economically extractab
The leachability tests for manufacturing scrap TV boards (STVB) have indicated the release of metals beyond the limit levels with potential problems f
Printed circuit boards (PCBs) from electronic gadgets at the end of their useful life period are currently being dumped in landfills or incinerated, c
Chiranjib Kumar Gupta
This book provides a comprehensive overview of the field of chemical metallurgy, addressing both common and less common metals. The objective of the v