2025 Grudinsky Hydrochloric Acid Leaching of Zinc Kiln Slag

The limited availability of high-quality ore deposits and the environmental hazards of metallurgical wastes highlight the importance of developing resource-efficient metal recovery technologies. Zinc kiln slag (ZKS), also known as Waelz slag, a by-product material enriched in non-ferrous metals, was processed through oxidative HCl leaching with H2O2 as an oxidant. Thermodynamic simulation and laboratory experiments were applied to determine optimal leaching conditions to dissolve copper, zinc, and iron. Optimal leaching efficiency was achieved with consumptions of 0.8 g HCl and 0.1 g H2O2 per gram of ZKS, a liquid-to-solid (L/S) ratio of 5 mL/g, a temperature of 70 °C, and a duration of 180 min, which resulted in recoveries of 96.3% Cu, 93.6% Fe, and 76.8% Zn. The solid residue with 43.5 wt.% C is promising for reuse as a reductant material in pyrometallurgical processes. Copper and arsenic were separated from the leachate via cementation with iron powder, achieving recovery rates of 98.9% and 91.2%, respectively. A subsequent two-step iron precipitation produced ferric hydroxide with 52.2 wt.% Fe and low levels of impurities. As a result, the developed novel hydrochloric acid oxidative leaching and metal precipitation route for ZKS recycling provides an efficient and sustainable alternative to conventional treatment methods.