In this study, maximum recovery of zinc and minimum recovery of iron from shaking table residue has been investigated. The residue is discarded as tailing of shaking table Tajkooh processing zinc–lead carbonate ores. The zinc plant residue containing 14.67% Zn, 5.93% Pb, and 10.47% Fe was blended with H2SO4. The orthogonal array L9 (34) comprising four parameters at three levels was chosen. The parameters and their levels were as: pH : 1, 1.5 and 2; time : 30, 45 and 60 min; temperature : 40, 60 and 80 °C; and solid/liquid ratio : 1:4, 1:6 and 1:8. The ultimate optimum leaching conditions were found to be Temperature :80 °C, solid/liquid ratio : 1:8, time : 60 min and pH=1. Under these conditions, recovery for zinc and iron was 83.5% and 1.3%, respectively. It was observed that the leaching rate of zinc increased with increasing temperature and time and decreasing pH without influence of S/L.
@article{2f936856-1ef5-47db-a01d-a7c24e28a16c,
title={Zinc leaching optimization},
author={H. Kamran Haghighi and D. Moradkhani},
year={2026},
language={en}
}TY - JOUR TI - Zinc leaching optimization AU - H. Kamran Haghighi AU - D. Moradkhani PY - 2026 LA - en ER -
The leachability tests for manufacturing scrap TV boards (STVB) have indicated the release of metals beyond the limit levels with potential problems f
Printed circuit boards (PCBs) from electronic gadgets at the end of their useful life period are currently being dumped in landfills or incinerated, c
C.N. Mpinga, J.J. Eksteen
Platinum Group Metals (PGMs), often with associated gold, have very few occurrences where they are present in an ore deposit at economically extractab
Cleophace Ngoie Mpinga
The thesis investigates alternative extraction strategies for platinum group metals (PGMs) from low-grade, high-chromium oxidized ores, which are incr