The use of mechanical activation to enhance gold recovery from a CuPbZn complex sulfide concentrate was investigated. The effects of milling time, ball size, sample to ball ratio and milling speed on thiosulfate leaching were studied. Under optimum conditions of milling time 1 h, ball size 20 mm, sample to ball ratio 1/15 and mill speed 600 r/min, nearly 78% of sample is amorphized, particle size decreases from d10=30 µm to d90=8 µm, specific surface area increases from 1.3 m²/g to 4.6 m²/g and gold recovery enhances from 17.4% in non-activated sample to 73.26%. The results for the mechanically activated samples indicate that the changes in structural disordering of the gold-bearing spherolite brought about an increase in gold recovery in the process of thiosulfate leaching.
@article{367f1371-395d-4091-ae7c-86aa0fb59a1e,
title={Effect of mechanical activation on thios},
author={Mohsen HASHEMZADEHFIN and Jana FICERIOVÁ},
year={2026},
language={en}
}TY - JOUR TI - Effect of mechanical activation on thios AU - Mohsen HASHEMZADEHFIN AU - Jana FICERIOVÁ PY - 2026 LA - en ER -
Unknown, Unknown
This chapter discusses metal casting processes, highlighting the diversity and common characteristics among them. The objective is to elucidate the fu
Unknown, Unknown
This study focuses on the fundamental characteristics of solid iron, which is predominantly composed of iron atoms and provides a basis for understand
Ir. Méshac KIME ILUNGA
Ce document traite des procédés métallurgiques spéciaux, en mettant particulièrement l'accent sur l'extraction liquide-liquide, un processus mis au po