This study investigated the optimum conditions for the leaching of manganese-rich iron ore for subsequent beneficiation studies on a laboratory scale. The experiments were carried out by varying the concentration of H2SO4 solution and the leaching temperature. The properties of the iron ore were characterized by X-ray fluorescence (XRF), X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), as well as photo-micrographic examination. The leaching experiments demonstrated that ore leaching increased with rising acid concentration and temperature. About 78.9% of the iron ore reacted within 120 minutes using a 4M H2SO4 solution at a temperature of 80°C. The activation energy (Ea) and the order of reaction were determined to be 31.14 kJ/mol and 0.979, respectively. The leaching data were fitted to the shrinking core model, indicating that the experimental results followed a diffusion-controlled mechanism. The residual product at optimal leaching was appropriately characterized and was found to contain silicate compounds.
@article{6dd24a37-4a5e-4a3f-aa04-5de26758d02e,
title={Dissolution Kinetic Evaluation of Manganese-rich Iron ore by Sulphuric acid Solution},
author={Alafara Abdullahi Baba and Musa John Saliu},
year={2017},
language={en}
}TY - JOUR TI - Dissolution Kinetic Evaluation of Manganese-rich Iron ore by Sulphuric acid Solution AU - Alafara Abdullahi Baba AU - Musa John Saliu PY - 2017 LA - en ER -
C.N. Mpinga, J.J. Eksteen
Platinum Group Metals (PGMs), often with associated gold, have very few occurrences where they are present in an ore deposit at economically extractab
The leachability tests for manufacturing scrap TV boards (STVB) have indicated the release of metals beyond the limit levels with potential problems f
Printed circuit boards (PCBs) from electronic gadgets at the end of their useful life period are currently being dumped in landfills or incinerated, c
ROPAFADZO JAMAKANGA
Printed circuit boards (PCBs) from electronic gadgets at the end of their useful life period are currently being dumped in landfills or incinerated, c
İbrahim Sönmez, Kemal Şahbudak
Chalcopyrite (CuFeS2) is commonly used ore in the production of copper, but leaching of this ore is very slow and inefficient due to “passivation” dur