2017 Ding et al Microstructure Evolution Grey Cast Iron Directional Solidification

The solidification characteristics and microstructure evolution in grey cast iron were investigated through Jmat-Pro simulations and quenching performed during directional solidification. The phase transition sequence of grey cast iron was determined as L → L + γ → L + γ + G → γ + G → P (α + Fe3C) + α + G. The graphite can be formed in three ways: directly nucleated from liquid through the eutectic reaction (L → γ + G), independently precipitated from the oversaturated γ phase (γ → γ + G), and produced via the eutectoid transformation (γ → G + α). The area fraction and length of graphite as well as the primary dendrite spacing decrease with increasing cooling rate. Type-A graphite is formed at a low cooling rate, whereas a high cooling rate results in the precipitation of type-D graphite. After analyzing the graphite precipitation in the as-cast and transition regions separately solidified with and without inoculation, we concluded that, induced by the inoculant addition, the location of graphite precipitation changes from mainly the γ interdendritic region to the entire γ matrix. It suggests that inoculation mainly acts on graphite precipitation in the γ matrix, not in the liquid or at the solid–liquid front.