2026 Farcean Alkaline leaching of electric arc furnace dust

Steel dust is a waste generated during steelmaking in an electric arc furnace (EAF), which contains a high proportion of iron-bearing compounds, leading to the inclusion of this waste as a resource in the circular economy for steelmaking. In addition to the limitation related to granulation (the waste must be processed to obtain larger particle sizes), a limiting factor is the increasingly high Zn content due to the low-quality ferrous charge. For the recycling of steelmaking dust, preliminary processing is necessary to reduce zinc. The paper presents, in addition to qualitative characterization of steel dust, laboratory experiments on the compositional changes associated with zinc redistribution applying the hydrometallurgical leaching process in an alkaline environment, using sodium hydroxide (NaOH). The changes in the chemical composition were identified and evaluated using X-ray fluorescence (XRF) and energy-dispersive X-ray spectroscopy (EDX). The experiments consisted of treating steel dust samples with 5 M NaOH at 25, 70, 80 and 90 ◦C for 60 min, using solid-to-liquid ratios of 10, 15, and 25 g/L. The results indicate a reduction in ZnO content ranging from 4.52% to 16.82%, as determined from Na2O-free normalization data. Room-temperature samples show only marginal changes in ZnO content. The XRF and EDX analyses indicate a moderate and condition-dependent redistribution of zinc in the solid phase after alkaline treatment, as evaluated using Na2O-free normalized data.