2017 Songtao Yang Effects of Dolomite on Mineral Compositions and Metallurgical Properties of Chromium Bearing Vanadium Tit min7110210

Chengde chromium-bearing vanadium–titanium magnetite (CCVTM) has been used as an important mineral resource in sinter making. The MgO content of this sinter can be enhanced by adding dolomite, which improved operation of the blast furnace. The effects of MgO on the form of dolomite on metallurgical properties, microstructure, and mineral compositions of CCVTM sinter were studied by a sinter pot test, X-Ray Diffraction (XRD), Scanning Electron Microscope (SEM), and mineral phase microanalysis. The results were as follows: The flame front speed and sinter coefficient decreased with an increase in MgO content from 2.66 to 3.86% by adding dolomite. With an increase in MgO content from 2.66 to 3.86%, the flame front speed, sintering utilization factor, and the value of RI decreased, while RDI and the softening–melting properties improved. In addition, the value of sinter strength (TI) reached a maximum value at MgO = 3.56%. An increase in the abundance of magnetite, magnesium ferrite, and silicate phase, as well as a decrease in hematite, was found with an increase in MgO content. We concluded that the most appropriate MgO content in the sinter is 3.56%.