Hydrometallurgical Extraction of Copper and Cobalt from Oxidised Copper-Cobalt Ore Using Ammonia Solution

Traditionally, copper and cobalt are extracted from oxidised ores via hydrometallurgical processing route. The ore is leached in sulphuric acid in reducing conditions. This method co-extracts impurity metal values like iron and manganese, necessitating downstream solution purification, which causes significant valuable losses. Pregnant leach solution purification is performed through step-wise oxidation and acid neutralisation of the leach solution. Cobalt is the most affected component in this process due to high losses incurred during the precipitation stages. Moreover, because the lixiviant is not recycled, the method consumes ominously high quantities of sulphuric acid. As a result, the process must be accompanied by readily available and cost-effective acid-making plant. In the event of an increase in the price of sulphuric acid raw materials or a decline in the ore grade, a source of 50% of the world’s cobalt might be rendered impracticable. This work investigates the viability of using ammoniacal solution as an alternative lixiviant to sulphuric acid. Ammoniacal solution forms soluble complexes with copper and cobalt at pH and potential where iron, manganese and other impurities tend to form precipitates. Because of the preferential leaching, downstream solution purification can be circumvented, thereby reducing valuable losses. Furthermore, because there is no solution altering, multi-step solution purification required, the leach solution retains its initial pre-leaching properties, making it fully recyclable. The recyclable nature of the lixiviant thus reduces lixiviant costs. Furthermore, an advantage of leaching in ammonia is lower equipment costs because ammonia is less corrosive than acid. The feed material used in this study was an oxidised copper-cobalt ore sourced from Katanga Region in the DRC. A size fraction analysis was undertaken in order to determine the deportation of the copper and cobalt metals in the feed material. In the leaching tests conducted, the effect of particle size, temperature, concentration of the reducing agent and concentrations of ammonia and ammonium carbonate were investigated.