Yu Lu, Dafeng Wang
Laser-MIG hybrid welding and MIG welding were carried out on 7B52 aluminum alloy, and the microstructure and mechanical properties of the joints were compared and analyzed. The results show that the average grain sizes of laser-MIG hybrid welding, MIG welding, and the laser weld zone are 18.38 µm, 24.16 µm, and 15.96 µm, respectively. The width of the HAZ of the laser zone is lower than that of the laser-MIG hybrid welding zone and MIG welding zone. The hardness is higher than that of the hybrid welding zone and MIG welding zone. The tensile strength of each laser-MIG hybrid welding joint zone is better than that of the MIG welding zone. The tensile strength of the laser zone is the worst. When stress ratio R = 0.1 and fatigue cycle Nf = 106, the fatigue strength of the laminated zone of the laser-MIG hybrid welding joint is better than that of the MIG welding joint, and the welding defect is the leading cause of fatigue cracks.
@article{b06e64c0-fb6d-4877-9ca2-212077126a13,
title={Comparative Analysis of Mechanical Properties and Microstructure of 7B52 Aluminum Alloy Laser-MIG Hybrid Welding and MIG Welding Joints},
author={Yu Lu and Dafeng Wang},
year={2024},
language={English}
}TY - JOUR TI - Comparative Analysis of Mechanical Properties and Microstructure of 7B52 Aluminum Alloy Laser-MIG Hybrid Welding and MIG Welding Joints AU - Yu Lu AU - Dafeng Wang PY - 2024 LA - English ER -
Regita Bendikiene, Antanas Ciuplys
The influence of the austempering temperatures on the microstructure and mechanical properties of austempered ductile cast iron (ADI) was investigated
Teodor Machedon-Pisu, Mihai Machedon-Pisu
In many areas such as the automotive, aircraft, and building industries, the high-strength aluminum alloy Al 7075 is frequently used due to its approp
Zhenwei Xie, Liexing Zhou
Enhancing the strength and toughness of aluminum alloys using microstructure optimization remains a key challenge. In this study, an AA2024 aluminum a
Qilun Li, Xiaobo Zhang
Hot extrusion forming is one of the best cost-effective processing methods to obtain high-strength aluminum alloys. In order to obtain high performanc
Muhammad R. R. Fatih, Hou-Jen Chen
Martensitic stainless steel (MSS) is widely used in several parts of automobiles where high strength, hardness, and corrosion resistance are required.
Koh-ichi Sugimoto
This article introduces the microstructural and mechanical properties of low and medium-carbon advanced martensitic steels (AMSs) subjected to heat-tr