Ridha Mnif, Mohamed Kchaou
Fatigue behavior of brass was studied at a constant deformation rate of 5.6 x 10-3 s-1 to understand the cyclic behavior and fatigue life under cyclic torsional deformation. Strains were in the range of 0.35 to 4.2%. In the as-drawn condition, it was found that the cyclic hardening/softening behavior strongly depends on the strain amplitude. For low strain amplitude, cyclic saturation occurred after an initial cyclic hardening stage, but for high strain amplitude, saturation could not be reached. Cyclic stress-strain (CSS) curve showed the presence of three distinct regions with a short quasi-plateau region in the intermediate amplitude range. Quantitative fatigue damage was assessed by microscopic observations of surface cracks.
@article{b2b7304a-4ec8-4f52-8db2-f6f019f1ce3f,
title={Cyclic Behavior and Damage Analysis of B},
author={Ridha Mnif and Mohamed Kchaou},
year={2026},
language={en}
}TY - JOUR TI - Cyclic Behavior and Damage Analysis of B AU - Ridha Mnif AU - Mohamed Kchaou PY - 2026 LA - en ER -
Unknown, Unknown
This chapter discusses metal casting processes, highlighting the diversity and common characteristics among them. The objective is to elucidate the fu
Unknown, Unknown
This study focuses on the fundamental characteristics of solid iron, which is predominantly composed of iron atoms and provides a basis for understand
Ir. Méshac KIME ILUNGA
Ce document traite des procédés métallurgiques spéciaux, en mettant particulièrement l'accent sur l'extraction liquide-liquide, un processus mis au po
Copper solvent extraction units at large hydrometallurgical plants face constraints in metal recovery, phase disengagement, and reagent consumption, d
Non spécifié
L'hydrométallurgie du cuivre, principalement axée sur les minerais oxydés facilement solubles, s'applique également aux minerais sulfurés ou mixtes ap