Zamukwanda Gambu, Peter Madindwa Mashinini
The purpose of the research is to determine the fatigue life of friction-welded 316L stainless steel joints. This was done by means of experimental testing and the stress-life method. Specimens were welded using a rotary friction welding process. Parameters such as friction pressure, forging pressure, forging time, and burn-off were kept constant, while rotational speed was varied (1500 rpm, 1800 rpm, 2100 rpm). After the specimens were welded, a flash was removed using a CNC lathe machine. An Amsler RBM 12 bending fatigue machine was used to determine the fatigue life of 316L stainless steel specimens. These specimens were subjected to a stress of 286.981MPa, 229.585 MPa, 172.189 MPa, and 133.925 MPa. The results obtained were plotted on the stress-life (S-N) curve. A microstructure and chemical element analysis was carried out on the three samples which were welded with a speed of 1500 rpm, 1800 rpm, and 2100 rpm. Fracture surface analysis was carried out using Olympus DSX500 and SEM JSM-IT100 microscopy. From the results obtained, it was discovered that all the specimens welded with a speed of 1500 rpm fractured when they were subjected to four different bending stresses. However, specimens welded at 1800 rpm and 2100 rpm fractured only at the highest applied stress of 286.981 MPa, while tests conducted at 229.585 MPa.
@article{bafcb60e-2802-42fa-ae6c-43c8ad01fa9c,
title={2026 Gambu Friction Welded 316L Fatigue},
author={Zamukwanda Gambu and Peter Madindwa Mashinini},
year={2026},
language={en}
}TY - JOUR TI - 2026 Gambu Friction Welded 316L Fatigue AU - Zamukwanda Gambu AU - Peter Madindwa Mashinini PY - 2026 LA - en ER -
Unknown, Unknown
This chapter discusses metal casting processes, highlighting the diversity and common characteristics among them. The objective is to elucidate the fu
Robert J. Hamlin
This thesis investigates the microstructural evolution and mechanical properties of simulated heat affected zones (HAZ) in cast precipitation hardened
G.E. Hicho, W.J. Boettinger
This study examines a mishap section and other selected sections made from 17-7 precipitation hardening stainless steel, revealing an unusually large
G.E.Hicho, W.J.Boettinger
We have examined the failed or "mishap" section, and other selected sections made from 17-7 precipitation hardening stainless steel, and have conclude
This paper addresses the challenge of assessing the feasibility of wind power plant projects at sites with insufficient or no local historic wind data