The leaching kinetics of hemimorphite (Zn4Si2O7(OH)2·H2O) in ammonium chloride solution was presented in detail. Effects of stirring speed (150–350 rpm), leaching temperature (75–108 °C), particle size of hemimorphite (45–150 µm), and the concentration of ammonium chloride (3.5–5.5 mol/L) on the zinc extraction rate were studied. The zinc extraction rate enhanced slightly with the increase in stirring speed, but increased significantly with an increase in the leaching temperature and ammonium chloride concentration. Zinc extraction was enhanced significantly in the first 60 min with decreasing particle size, but had little effect on the leaching process after 60 min. Scanning electron microscopy (SEM) analysis showed that some silica gel formed in the leaching process was not separated from the hemimorphite surface, but covered some of the active particle surface. The Elovich equation successfully described the leaching kinetics of hemimorphite in ammonium chloride solution with an apparent activation energy of 405.14 kJ/mol at temperatures of 75–90 °C and 239.61 kJ/mol at temperatures of 95–108 °C, which is characteristic for a chemically-controlled process. Silica gel is generated at temperatures of 75–90 °C and decomposed into silica at temperatures of 95–108 °C.
@article{cf0f63a7-f2d3-4b81-94d7-ebbecf3d7d43,
title={2017 Zhao Hemimorphite leaching kinetics in ammonium chloride},
author={Duoqiang Zhao and Shenghai Yang},
year={2026},
language={en}
}TY - JOUR TI - 2017 Zhao Hemimorphite leaching kinetics in ammonium chloride AU - Duoqiang Zhao AU - Shenghai Yang PY - 2026 LA - en ER -
The leachability tests for manufacturing scrap TV boards (STVB) have indicated the release of metals beyond the limit levels with potential problems f
Printed circuit boards (PCBs) from electronic gadgets at the end of their useful life period are currently being dumped in landfills or incinerated, c
Chiranjib Kumar Gupta
This book provides a comprehensive overview of the field of chemical metallurgy, addressing both common and less common metals. The objective of the v
Alain Vignes
This book provides a comprehensive overview of the fundamental principles of extractive metallurgy, with a specific focus on basic thermodynamics and
Martina Laubertová, Bora Derin, Jarmila Trpčevská, Klaudia Šándorová and Emília Sminčáková
This study was performed to investigate the possibility of copper recovery from the waste printed circuit boards (WPCBs) of waste mobile phones using